AISI 4340 steel is a medium carbon, low alloy steel known for its toughness and strength in relatively large sections. AISI 4340 is also one kind of nickel chromium molybdenum steels. 4340 alloy steel is generally supplied hardened and tempered in the tensile range of 930 – 1080 Mpa.

vera.liang@ztwysteel.com 메시지

제품 상세 정보

AISI 4340 Steel Specification and Relevant Standards

Country	USA	Britain	Britain	Japan
표준	ASTM A29	EN 10250	BS 970	JIS G4103
성적	4340	36CrNiMo4/ 1.6511	EN24/817M40	SNCM 439/SNCM8

ASTM 4340 Steels And Equilvalents Chemical Composition

표준	Grade	C	Mn	P	S	Si	Ni	Cr	Mo
ASTM A29	4340	0.38-0.43	0.60-0.80	0.035	0.040	0.15-0.35	1.65-2.00	0.70-0.90	0.20-0.30
EN 10250	36CrNiMo4/ 1.6511	0.32-0.40	0.50-0.80	0.035	0.035	≦0.40	0.90-1.20	0.90-1.2	0.15-0.30
BS 970	EN24/817M40	0.36-0.44	0.45-0.70	0.035	0.040	0.1-0.40	1.3-1.7	1.00-1.40	0.20-0.35
JIS G4103	SNCM 439/SNCM8	0.36-0.43	0.60-0.90	0.030	0.030	0.15-0.35	1.60-2.00	0.60-1.00	0.15-0.30

AISI Alloy 4340 Steel Mechanical Properties

Mechannical Properties (Heat Treated Condition )	Condition	Ruling section mm	Tensile Strength MPa	Yield Strength MPa	Elong. %	Izod Impact J	Brinell Hardness
	T	250	850-1000	635	13	40	248-302
	T	150	850-1000	665	13	54	248-302
	U	100	930-1080	740	12	47	269-331

	V	63	1000-1150	835	12	47	293-352
	W	30	1080-1230	925	11	41	311-375
	X	30	1150-1300	1005	10	34	341-401

	Y	30	1230-1380	1080	10	24	363-429
	Z	30	1555-	1125	5	10	444-

Thermal Properties

Properties	Metric	Imperial
Thermal expansion co-efficient (20°C/68°F, specimen oil hardened, 600°C (1110°F) temper	12.3 µm/m°C	6.83 µin/in°F
Thermal conductivity (typical steel)	44.5 W/mK	309 BTU in/hr.ft².°F

Forging of 4340 Alloy Steel

Preheat the steel 4340 first, heat up to 1150°C – 1200°C maximum for forging, hold until temperature is uniform throughout the section.

Do not forge below 850 °C. 4340 has good forging characteristics but care must be taken when cooling as the steel shows susceptibility to cracking. Following forging operation the work piece should be cooled as slowly as possible. And cooling in in sand or dry lime is recommended etc.