AISI 4340 stål / 36CrNiMo4 / 1.6511 / EN24 / 817M40 / SNCM439

kategori

Seneste blogs

Grain oriented steel coil guide

Transformer Oriented Steel Sheet: High Performance Sheet Solution

The Impact of Plate Ductility on Manufacturing and Shaping Processes

Silicon Steel Materials in Various Production Scenarios

Professional Insights into the Mechanical Strength of Tin-Plated Steel Coils

The Effectiveness of Passivation Treatment on Tinplate and Common Technical Aspects

Explanation of Key Coating Thickness Parameters in Tinplate Manufacturing

Customized Steel Solution in XX Project: A Case Study

Key Points for Selecting Raw Material Base Materials for Tinplate

Detailed Explanation of the Basic Definition and Material Structure of Tinplate

China Silicon Steel Manufacturer & Exporter | High-Quality Steel Products | Baowu

AISI 4340 stål / 36CrNiMo4 / 1.6511 / EN24 / 817M40 / SNCM439

AISI 4340-stål er et medium kulstofholdigt, lavlegeret stål, der er kendt for sin sejhed og styrke i relativt store sektioner. AISI 4340 er også en slags nikkel-krom-molybdæn-stål. 4340 legeret stål leveres generelt hærdet og anløbet i trækstyrkeområdet 930 - 1080 Mpa.

Detaljer om produktet

AISI 4340 stålspecifikation og relevante standarder

Land	USA	Storbritannien	Storbritannien	Japan
Standard	ASTM A29	EN 10250	BS 970	JIS G4103
Karakterer	4340	36CrNiMo4/ 1.6511	EN24/817M40	SNCM 439/SNCM8

ASTM 4340 Stål og tilsvarende kemiske sammensætninger

Standard	Karakter	C	Mn	P	S	Si	Ni	Cr	Mo
ASTM A29	4340	0.38-0.43	0.60-0.80	0.035	0.040	0.15-0.35	1.65-2.00	0.70-0.90	0.20-0.30
EN 10250	36CrNiMo4/ 1.6511	0.32-0.40	0.50-0.80	0.035	0.035	≦0.40	0.90-1.20	0.90-1.2	0.15-0.30
BS 970	EN24/817M40	0.36-0.44	0.45-0.70	0.035	0.040	0.1-0.40	1.3-1.7	1.00-1.40	0.20-0.35
JIS G4103	SNCM 439/SNCM8	0.36-0.43	0.60-0.90	0.030	0.030	0.15-0.35	1.60-2.00	0.60-1.00	0.15-0.30

AISI Alloy 4340 stål Mekaniske egenskaber

Mekaniske egenskaber (Varmebehandlet tilstand)	Tilstand	Afgørende sektion mm	Trækstyrke MPa	Udbyttestyrke MPa	Elong. %	Izod Impact J	Brinell Hårdhed
	T	250	850-1000	635	13	40	248-302
	T	150	850-1000	665	13	54	248-302
	U	100	930-1080	740	12	47	269-331

	V	63	1000-1150	835	12	47	293-352
	W	30	1080-1230	925	11	41	311-375
	X	30	1150-1300	1005	10	34	341-401

	Y	30	1230-1380	1080	10	24	363-429
	Z	30	1555-	1125	5	10	444-

Termiske egenskaber

Ejendomme	Metrisk	Imperial
Termisk udvidelseskoefficient (20 °C/68 °F, prøve oliehærdet, 600 °C (1110 °F) tempereret)	12,3 µm/m°C	6,83 µin/in°F
Varmeledningsevne (typisk stål)	44,5 W/mK	309 BTU in/hr.ft².°F

Smedning af 4340 legeret stål

Forvarm først stålet 4340, varm op til 1150°C - 1200°C maksimalt til smedning, hold indtil temperaturen er ensartet i hele sektionen.

Må ikke smedes under 850 °C. 4340 har gode smedeegenskaber, men der skal udvises forsigtighed ved afkøling, da stålet er tilbøjeligt til at revne. Efter smedningen skal arbejdsemnet afkøles så langsomt som muligt. Og afkøling i sand eller tør kalk anbefales osv.

Udfyld venligst dit navn, din e-mail og din besked nedenfor. Vi vil læse dine oplysninger omhyggeligt og svare dig så hurtigt som muligt. Tak for din kontakt og støtte.